L. Grigorjeva , D. Millers , K. Smits , A. Sarakovskis , W. Lojkowski , A. Swiderska-Sroda , W. Strek ,
Transparent Ce and Ce/Pr doped YAG ceramics were prepared under high pressures (up to 8 GPa) and relative
low temperature (450 C). Grain size of the ceramics is less than 50 nm. However unknown defects
or disorders strains on grain boundaries caused the additional absorption in these ceramics. The luminescence
intensity, spectra and the decay time dependence on pressure applied during ceramic preparation
were studied. Concentration of some intrinsic point defect was reduced under the high pressure applied
for sintering process.
It is shown that formation time of the excited state of Ce luminescence depends on the pressure applied
during ceramic sintering.
Optical Materials 34 (2012) 986–989