Radioluminescence, thermoluminescence and dosimetric properties of ZnO ceramics

Larisa Grigorjeva, Aleksejs Zolotarjovs, Sergej Yu Sokovnin, Donats Millers, Krisjanis Smits, Vladislav G. Il`ves

Two types of ZnO ceramics were fabricated and characterized by XRD, SEM methods. The radioluminescence spectra were measured within the 300–550 K range. The defect luminescence band peaking at ~2.35 eV is the dominant one in radioluminescence spectra in both of the fabricated ceramics. The thermostimulated luminescence (TSL) glow-curves were measured after X-ray irradiation at 300 K. It was concluded that the complex overlapping peak within the 320–450 K temperature range consists of two components (~360–375 K and 400–420 K). The ratio of component intensities differs in both ceramics. The positions of high temperature TSL components (480–520 K) also differ in both samples; therefore not only sintering conditions but also the properties of the initial powder are very important for characteristics of TSL. A linear dependence of peak intensity on irradiation dose was observed up to ~3 kGy for ceramic 1 and up to 9 kGy for ceramic 2.

cer_int_2017_img

Ceramics International

DOI: 10.1016/j.ceramint.2017.02.016

pdf-icon Download PDF